BAMBU LAB
Bambu Lab PLA Basic
Bambu Lab PLA Basic Filament
High-printing Quality
RFID for Intelligent Printing
Printing Speed <300 mm/s
Nozzle Temperature 190 - 230 °C
Bed Temperature 35 - 45 °C
BAMBU LAB
Bambu Lab PLA CMYK Lithophane Bundle
Bambu Lab PLA CMYK Lithophane Bundle
MakeMake Colorful 3D Models
Include Jade White,Basic Yellow,Basic Magenta,Basic Cyan
Recommended Printing Temperature: 210 - 230 °C
Recommended Bed Temperature: 45 - 60°C
Compatible With All kind of 3D Printer
Density 1.24 g/cm3
BAMBU LAB
Bambu Lab PLA Metal
Bambu Lab PLA Metal
Metal Surface Texture & Metallic Shine
High impact strength
Recommended Printing Temperature: 210 - 230 °C
Recommended Bed Temperature: 45 - 60°C
Compatible With All kind of 3D Printer
Density 1.24 g/cm3
BAMBU LAB
Bambu Lab PLA Matte
Bambu Lab PLA Matte
Matte Surface Texture
Recommended Printing Temperature: 210 - 230 °C
Recommended Bed Temperature: 45 - 60°C
Compatible With All kind of 3D Printer
Density 1.24 g/cm3
Polymaker
Polymaker PolyTerra PLA
Polymaker PolyTerra PLA
Eco-Friendly
A World of Color & Effects
Printing Speed 30mm/s - 70mm/s
Prop Bed Temperature: 25˚C - 60˚C
Printing Temperature: 190˚C - 230˚C
Jam-Free Technology
Polymaker
Polymaker PolySonic PLA Pro
Polymaker PolySonic PLA Pro
High-speed Printing up to 300 mm/s
Impact resistance like ABS
Prop Extruder Tempo 210 - 230 °C
Prop Bed Temp 25 - 60 °C
Polymaker
Polymaker PolySonic PLA
Polymaker PolySonic PLA
High-speed 3D printing filament
Nozzle Temp 210~230°C
Bed Temp 30~60°C
Printing Speed up to 300mm/s
Density 1.23 g/cm3
Glass transition temperature 59°C
Polymaker
Polymaker PolyFlex TPU90
Polymaker PolyFlex TPU90
Created from Covestro’s Addigy
Density 1.12 g/cm3
Tensile strength 30.0 ± 0.66 MPa
Elongation at break 528 586.8 ± 15.3 %
Shore hardness 90A
Nozzle temperature 210 – 230℃
Build plate temperature 25~60℃
Polymaker
Polymaker PolyLite PLA
Polymaker PolyLite PLA Filament
Density 1.17 g/cm3
Elongation at break 1.90 ± 0.21 %
Charpy impact strength 2.68 ± 0.16 kJ/m2
Tensile strength 46.6 ± 0.9 MPa
Nozzle temperature 190 – 230℃
Build plate temperature 25 - 60˚C
Printing speed 40-60mm/s
Polymaker
Polymaker PolyLite Dual Silk PLA
PolyLite Dual Silk PLA Filament
Density 1.17 g/cm3
Tensile strength 46.6 ± 0.9 MPa
Elongation at break 1.90 ± 0.21 %
Charpy impact strength 2.68 ± 0.16 kJ/m2
Nozzle temperature 190 – 230℃
Build plate temperature 25 - 60˚C
printing speed 40-60mm/s